One Component Epoxy Compound
Epoxy Adhesive 1K is a single component Epoxy Resin based compound developed for Auto Electrical, Electronics and Medical applications
- Tertiary Amine Hardner based system
- Excellent Thixotropy
- Good adhesive properties and flexibility
- Long shelf life
- Faster curing
- Excellent Adhesion to Plastics and Metals
Properties
- Cable Fittings
- URECAST-FR is ideally used in the manufacture of cable sleeves and sealing ends
- Color and Appearance : Coloured*, thixotropic, paste consistency
- Viscosity mPa.s at 27°C : 40,000 - 1,00,000
Method Of Application
- The compound could be applied by Dispenser, spatula or brush on the preheated component.
Curing Schedule
- 100°C/ 40 min OR 130°C / 30 min
Uses
- Armature coating of starter motors
- For fixing components of magnetos
- Disposable syringe needle joining
Storage Condition And Shelf Life
- The Epoxy Adhesive 1K has Shelf life of 1 month if stored at temperature of between 15 to 20°C
Safe Handling
- Epoxy Adhesive 1K has hardly any effect on the skin & mucous membrane. Direct contact, however, should be avoided by using rubber gloves & goggles. Affected area of the skin should be scrubbed with 5% acetic and washed with plenty of water & soap.
Packing
- 1kg, 4 kg, in MS Tins
- * Available in Red/White/ Blue colour
Salient Features
- Epoxy Adhesive 1K is a one component, coloured , heat curing epoxy resin compound. No Hardner is required to be added externally, since this is already incorporated. Epoxy Adhesive 1K is thixotropic and available in paste consistency Epoxy Adhesive 1K is suitable for consolidation of windings of electrical machines such as rotors of alternators. Epoxy Adhesive 1K can be applied by brushing or spatula. Warming of Epoxy Adhesive 1K up to 60 & 70°C during application may facilitate during interlayer brushing application
Properties Of Epoxy Adhesive 1k (Typical)
| Parameter | Observation |
|---|---|
| Color | Black |
| Type | One Component Epoxy |
| No of Component | One |
| Viscosity | Thick Thixotropic Paste |
| Thermal Conductivity | 0.6 -0.7 w/m –degree k |
| Electrical conductivity | Electrically Insulating |
| Continues usable temp | >155 °C continuous for 20,000 hrs |
| Resistance to thermal cycling | 10 cycles of -40 to +150 |
| Flash Point (TCC) °C | > 150 °C |
| Coefficient of thermal expansion | 180-200x10E-6mm/mm/°C |
| Chemical Resistance | Good |
| Specific Gravity | 1.6 g/cc |
| Glass Transition temp | 130 °C |
| Temperature Resistance | 200 for short period (60min) |
| Storage temp | Below 10 °C |
| Hardness ,Shore D@ 25 °C | > 80 |
| Water absorption | < 0.2 % |
| Volume resistivity (ohm.cm) | 1.00E+14 |
| Dielectric Strength | 17 kV/mm |
| Dielectric Constant | 3.0 |
| Geltime (120 °C) | 30 min |
| Curing Condition | 150 °C / 60 min |
| Moisture Content | < 0.1 % |
| Shelf life | 1 month at 20 °C |